1, galvanized silk mesh molding sheet must be packed with flat hard materials, to avoid improper packaging and cause eternal deformation. It is important that each package and roll of raw material be marked with product name, standard, quantity, trademark, lot number, manufacturer, date of production, packing symbol, inspector code and inspection certificate.
1, galvanized wire mesh molding sheet must be packed with flat hard data, to avoid eternal deformation due to poor packaging. It IS VERY IMPORTANT THAT EACH PACKAGE AND ROLL OF RAW SHEET MATERIAL BE MARKED WITH PRODUCT NAME, STANDARD, QUANTITY, TRADEMARK, batch number, MANUFACTURER, DATE of production, STACKING SYMBOL, INSPECTOR CODE AND INSPECTION CERTIFICATE.
Galvanized hook mesh selection of low carbon steel wire, the surface of cold galvanized or hot galvanized anticorrosive treatment, strong mesh, strong protection, long anticorrosive time. Galvanized wire hook nets are widely used, widely used in warehouses, refrigeration between things, protective reinforcement, parks, zoos, Marine fishing fences and construction site fences, mechanical equipment protection.
Hot-dip galvanized wire is widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transmission, shipbuilding and other industries. It has been widely used in recent years in agricultural fields such as agricultural medicine sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and so on.
Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.
Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.
In GENERAL, THE HARDNESS OF A METAL IS OFTEN CONSIDERED AS THE RESISTANCE OF a MATERIAL TO COMPRESSION PLASTIC deformation, scratches, wear, or cutting. In the adjustment of zinc dip distance of galvanized wire, keep the original speed unchanged, according to the time of zinc dip, wire diameter, and then estimate the zinc dip distance. By adjusting the zinc dipping distance, the zinc dipping time of various specifications of steel wire is shortened by 5s on average compared with that before debugging, so that the zinc consumption is reduced, the zinc consumption per ton of steel wire is reduced from the original 61kg to 59.4kg.
1, want to a person or friends together, leave the dog a person at home, so that it will not be hurt, the dog is comfortable, safe, but not because of loose and develop bad habits, at this time you can use the pet cage.
If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.
The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.